摘要The effects of environment and fatigue on the electrical resistance and piezoresistivity of the carbon nanotube/cement composite is investigated under a service environment using a four-probe method. The main influencing factors include temperature (20, 30, 40℃, and 50℃), water content (0%-6.4%), temperature and water content coupling, and number of fatigue cycles (20, 40, 60, 110, 160, and 240×103). Test results showed that environment and fatigue considerably affected resistivity and piezoresistivity. The resistivity of the composite decreased as water content increased. When water content changed from 1.3% to 5.8%, resistivity was reduced 43%. By contrast, piezoresistivity and change in resistance initially increased and then decreased as water content increased. Temperature substantially affected resistivity and piezoresistivity. As temperature increased, resistivity decreased but piezoresistivity increased. Electrical resistance and change in resistivity exhibited a strong linear relationship with temperatures ranging from 20℃ to 50℃ with an R2 of over 0.99. As temperature increased from 20℃ to 50℃, resistivity decreased 35% and change in resistivity increased 84%, thereby indicating improved piezoresistivity. Piezoresistive sensitivity to temperature demonstrated a strong negative linear relationship with water content with an R2 of 0.915. Electrical resistance and piezoresistivity increased as the number of cycles increased. The major causes of changes in resistivity and piezoresistivity are a change in tunneling conduction and the development of micro-cracks.
Abstract：The effects of environment and fatigue on the electrical resistance and piezoresistivity of the carbon nanotube/cement composite is investigated under a service environment using a four-probe method. The main influencing factors include temperature (20, 30, 40℃, and 50℃), water content (0%-6.4%), temperature and water content coupling, and number of fatigue cycles (20, 40, 60, 110, 160, and 240×103). Test results showed that environment and fatigue considerably affected resistivity and piezoresistivity. The resistivity of the composite decreased as water content increased. When water content changed from 1.3% to 5.8%, resistivity was reduced 43%. By contrast, piezoresistivity and change in resistance initially increased and then decreased as water content increased. Temperature substantially affected resistivity and piezoresistivity. As temperature increased, resistivity decreased but piezoresistivity increased. Electrical resistance and change in resistivity exhibited a strong linear relationship with temperatures ranging from 20℃ to 50℃ with an R2 of over 0.99. As temperature increased from 20℃ to 50℃, resistivity decreased 35% and change in resistivity increased 84%, thereby indicating improved piezoresistivity. Piezoresistive sensitivity to temperature demonstrated a strong negative linear relationship with water content with an R2 of 0.915. Electrical resistance and piezoresistivity increased as the number of cycles increased. The major causes of changes in resistivity and piezoresistivity are a change in tunneling conduction and the development of micro-cracks.
基金资助:Supported by the National Natural Science Foundation of China (No.51108247)
通讯作者:
LI Jin-lu
E-mail: ljl7103@163.com
引用本文:
李金路, 冯子强, 吴佳杰, 魏姗姗, 葛智. 环境及疲劳荷载作用下碳纳米管水泥基复合材料压敏性能研究[J]. Journal of Highway and Transportation Research and Development, 2018, 12(3): 16-21.
LI Jin-lu, FENG Zi-qiang, WU Jia-jie, WEI Shan-shan, GE Zhi. Effects of Environment and Fatigue on the Piezoresistivity of Carbon Nanotube/Cement Composite. Journal of Highway and Transportation Research and Development, 2018, 12(3): 16-21.
[1] CHEN P W, CHUNG D D L. Carbon Fiber Reinforced Concrete for Smart Structures Capable of Non-destructive Flaw Detection[J]. Smart Materials and Structures, 1993, 2(1):22-30.
[2] HAN B G, OU J P. Embedded Piezoresistive Cement-based Stress/strain Sensor[J]. Sensors and Actuators A:Physical, 2007, 138(2):294-298.
[3] ⅡJIMA S. Helical Microtubules of Graphitic Carbon[J]. Nature, 1991, 354(6348):56-58.
[4] RUOFF R S, TERSOFF J, LORENTS D C, et al. Radial Deformation of Carbon Nanotubes by Van der Waals Forces[J]. Nature,1993,364(6437):514-516.
[5] WANSOM S, KIDNER N J, WOO L Y, et al. AC-impedance Response of Multi-walled Carbon Nanotube/cement Composites[J]. Cement and Concrete Composites, 2006, 28(6):509-519.
[6] LI G Y, WANG P M, ZHAO X, et al. Pressure-sensitive Properties and Microstructure of Carbon Nanotube Reinforced Cement Composites[J]. Cement and Concrete Composites, 2007, 29(5):377-382.
[7] LI Geng-ying, WANG Pei-ming. Effect of Surface Treatment on Volume Resistance and Sensing Effect of Carbon Nanotube-reinforced Cement Composites[J]. Sichuan Building Science,2007,33(6):143-136.(in Chinese)
[8] LI Geng-ying, YANG Jing, ZENG Ling-bo, et al. Piezoresistivity of Carbon Nanotube-Cement Motars Modified by Styrene-Butadiene Rubber Emulsion[J]. Journal of Building Materials, 2013, 16(1):65-69.(in Chinese)
[9] LUO Jian-lin. Fabrication and Functional Properties of Multi-Walled Carbon Nanotube/Cement Composites[D]. Harbin:Harbin Institute of Technology, 2009.(in Chinese)
[10] HAN B G, YU X, OU J P. Effect of Water Content on the Piezoresistivity of MWNT/cement Composites[J]. Journal of Materials Science, 2010, 45(14):3714-3719.
[11] HAN B G, ZHANG K, YU X, et al. Electrical Characteristics and Pressure-sensitive Response Measurements of Carboxyl MWNT/cement Composites[J]. Cement and Concrete Composites, 2012, 34(6):794-800.
[12] JIANG Hai-feng. Self-sensing Carbon Nanotube Cement-based Composites and Their Application in Traffic Detection[D]. Harbin:Harbin Institute of Technology, 2009.(in Chinese)
[13] YAO Bin. Influence of Environmental Conditions on Piezoreresistive Effect of Carbon Nanotube Fiber Concrete[D]. Harbin:Harbin Institute of Technology, 2013.(in Chinese)
[14] MA Xue-ping. Piezoresistivity of Carbon Nanotubes-cement Composite[D]. Jinan:Shandong University, 2013.(in Chinese)
[15] ZUO Jun-qing. Research on Pressure-sensitive Properties of Carbon Nanotube-carbon Fiber/Cement Composites under Low Stress[J]. Fly Ash Comprehensive Utilization, 2013(2):12-15.(in Chinese)
[16] MENG Jing. Piezoresistive Properties and Conductive Mechanism of High Dispersion Carbon Nanotube-Cement Based Composites[D]. Harbin:Harbin Institute of Technology, 2014.(in Chinese)
[17] LIU Xiao-yan, LIU Yan, MING Wei, et al. Study on the Electrical Conductivity and Pressure Sensitive of Carbon Nanotubes/Cement-based Composite Materials[J]. Fly Ash Comprehensive Utilization, 2015(2):6-9.(in Chinese)
[18] LIU Xiao-yan, Fu Feng, LIU Jing, et al. Feasibility Research of Carbon Nanotube/cement Composites used for Structural Stress Monitoring[J]. Fly Ash Comprehensive Utilization, 2015(4):8-11.(in Chinese)
[19] WANG Qin, WANG Jian, LIU Bo-wei, et al. Stress-sensing Performance of MWCNTs Cement Composites[J]. Bulletin of the Chinese Ceramic Society,2016,35(9):2733-2740.(in Chinese)
[20] YU X, KWON E. Carbon Nanotube Based Self-Sensing Concrete for Pavement Structural Health Monitoring[R].Duluth:University of Minnesota Duluth, 2012.
[21] LI C, THOSTENSON E T, CHOU T W. Dominant Role of Tunneling Resistance in the Electrical Conductivity of Carbon Nanotube-based Composites[J]. Applied Physics Letters, 2007, 91(22):162-193.
[22] QIAO L, ZHENG W T, WEN Q B, et al. First-principles Density-functional Investigation of the Effect of Water on the Field Emission of Carbon Nanotubes[J]. Nanotechnology, 2007, 18(15):625-637.
[23] CHEN C W, LEE M H, CLARK S J. Gas Molecule Effects on Field Emission Properties of Single-walled Carbon Nanotube[J]. Diamond and Related Materials, 2004, 13(4):1306-1313.
[24] TOMBLER T W, ZHOU C W, ALEXSEYEV L, et al. Reversible Electromechanical Characteristics of Carbon Nanotubes under Local-probe Manipulation[J]. Nature,2000, 405(6788):769-772.
[1]
李宁, 马骉, 李瑞, 司伟. 基于PUMA的单级和多级加载模式下级配碎石性能研究[J]. Journal of Highway and Transportation Research and Development, 2019, 13(2): 1-12.
[2]
许海亮, 任合欢, 何兆才, 何炼. 车路耦合条件下沥青混凝土路面变形特性时域分析[J]. Journal of Highway and Transportation Research and Development, 2019, 13(2): 13-19.
[3]
杜健欢, 艾长发, 黄超, 郭玉金, 蒋运兵. 界面水对沥青复合小梁疲劳性能的影响试验[J]. Journal of Highway and Transportation Research and Development, 2019, 13(1): 1-7.
[4]
姚国强, 言志信, 龙哲, 翟聚云. 基于岩质边坡相似材料的锚固界面剪应力分布规律研究[J]. Journal of Highway and Transportation Research and Development, 2019, 13(1): 8-15.
[5]
刘泽, 何矾, 黄天棋, 蒋梅东. 车辆荷载在挡土墙上引起的附加土压力研究[J]. Journal of Highway and Transportation Research and Development, 2019, 13(1): 16-23.
[6]
詹健, 邵旭东, 曲宛桐, 曹君辉. 钢-STC轻型组合桥面结构多参数分析[J]. Journal of Highway and Transportation Research and Development, 2019, 13(1): 50-59.
[7]
邱欣, 徐静娴, 陶钰强, 杨青. 路面结冰条件判别标准及SVM预测分析研究[J]. Journal of Highway and Transportation Research and Development, 2018, 12(4): 1-9.
[8]
高伟, 崔巍, 李秀凤. 半刚性基层表面抗冲刷性能试验与分析[J]. Journal of Highway and Transportation Research and Development, 2018, 12(4): 10-17.
[9]
张向东, 任昆. 煤渣改良土路基的动弹性模量及临界动应力试验研究[J]. Journal of Highway and Transportation Research and Development, 2018, 12(4): 25-32.
[10]
刘栋, 尚小亮, 杨西海. 垃圾焚烧炉渣中可溶盐对水泥稳定材料性能的影响[J]. Journal of Highway and Transportation Research and Development, 2018, 12(4): 18-24.
[11]
李龙海, 杨茹. 多次加铺的复合道面疲劳寿命分析[J]. Journal of Highway and Transportation Research and Development, 2018, 12(3): 7-15.
[12]
蔡旭, 李翔, 吴旷怀, 黄文柯. 基于旋转压实的水泥稳定再生集料设计方法研究[J]. Journal of Highway and Transportation Research and Development, 2018, 12(3): 1-6.
[13]
田小革, 韩海峰, 李新伟, 吴栋, 魏东. 半刚性路面中双层半刚性基层的倒装效应[J]. Journal of Highway and Transportation Research and Development, 2018, 12(3): 22-27.
[14]
邢磊, 雷柏龄, 陈忠达, 戴学臻. 彩色沥青路面胶凝材料的制备技术[J]. Journal of Highway and Transportation Research and Development, 2018, 12(2): 1-6.
[15]
方薇, 陈向阳, 杨果林. 带齿格栅加筋挡墙工作机理的数值模拟研究[J]. Journal of Highway and Transportation Research and Development, 2018, 12(2): 7-13.
2018, Vol. 12 